[EN] Alkali-aluminosilicate glass |
| 71/73 |
Anmelder/Inhaber |
PA |
TAIWAN GLASS INC CORP, TW
;
TAIWAN GLASS IND CORP, TW
|
| 72 |
Erfinder |
IN |
BIENNECK LARS, DE
;
CARL GUNTER, DE
;
LIN CHIA-HUNG, TW
;
LINZ HANS-JUERGEN, DE
;
WILTZSCH SVEN, DE
|
| 22/96 |
Anmeldedatum |
AD |
13.11.2014 |
| 21 |
Anmeldenummer |
AN |
201414540684 |
|
Anmeldeland |
AC |
US |
|
Veröffentlichungsdatum |
PUB |
17.10.2017 |
33
31
32 |
Priorität |
PRC
PRN
PRD |
DE
102013019003
20131113
|
| 51 |
IPC-Hauptklasse |
ICM |
C03C 21/00
(2006.01)
|
| 51 |
IPC-Nebenklasse |
ICS |
B32B 17/00
(2006.01)
C03C 3/085
(2006.01)
C03C 3/095
(2006.01)
|
|
IPC-Zusatzklasse |
ICA |
|
|
IPC-Indexklasse |
ICI |
|
|
Gemeinsame Patentklassifikation |
CPC |
B32B 17/00
B32B 2457/20
C03C 21/002
C03C 3/085
C03C 3/095
Y10T 428/26
|
|
MCD-Hauptklasse |
MCM |
C03C 21/00
(2006.01)
|
|
MCD-Nebenklasse |
MCS |
B32B 17/00
(2006.01)
C03C 3/085
(2006.01)
C03C 3/095
(2006.01)
|
|
MCD-Zusatzklasse |
MCA |
|
| 57 |
Zusammenfassung |
AB |
[EN] The present disclosure relates to an alkali-aluminosilicate glass which contains between 47.5 and 55 wt.% SiO2, between 21 and 27.5% Al2O3; and between 12 and 16 wt.% Na2O. The molar ratio of Al2O3 and Na2O amounts to between 1:0.9 and 1:1.2. This glass is characterized by high hardness and high surface strengths after its chemical toughening, whereby the resulting extremely high scratch resistance favors its use as a display glass. A further preferred feature of this glass is its much lower viscosity for this group of glasses. |
| 56 |
Entgegengehaltene Patentdokumente/Zitate,
in Recherche ermittelt |
CT |
GB000001177248A
US000002779136A
US000003485647A
US000003485702A
US000003524737A
US000003752729A
US020110017297A1
US020110045961A1
US020120083401A1
US020120171497A1
US020120297829A1
US020130004758A1
US020130122284A1
US020130224491A1
US020130288001A1
US020140226090A1
WO002012099053A1
WO002013073685A1
|
| 56 |
Entgegengehaltene Patentdokumente/Zitate,
vom Anmelder genannt |
CT |
CN000001391538A
CN000101508524A
JP002013177305A
US000008075999B2
US020120321898A1
WO002013130646A1
|
| 56 |
Entgegengehaltene Nichtpatentliteratur/Zitate,
in Recherche ermittelt |
CTNP |
Taylor et al., “Properties of Soda Aluminosilicate Glasses: V, Low-Temperature Viscosities,” Journal of the American Ceramic Society, vol. 53, No. 12, p. 692-695, Dec. 1970. 0
|
| 56 |
Entgegengehaltene Nichtpatentliteratur/Zitate,
vom Anmelder genannt |
CTNP |
State Intellectual Property Office of the People's Republic of China, First Office Action Issued in Application No. 201410638271.X, Jul. 4, 2016, 11 pages. (Submitted with Partial Translation). 1
|
|
Zitierende Dokumente |
|
US000011167375B2
US000011426818B2
US000012122120B2
|
|
Sequenzprotokoll |
|
|
|
Prüfstoff-IPC |
ICP |
B32B 17/00
C03C 3/085
C03C 3/095
|